Structural, microstructural, and optical properties of Zn12xMgxO thin films grown onto glass substrate by ultrasonic spray pyrolysis

Simple item page
dc.contributor.authorK. Hoggas
dc.date.accessioned2024-02-16T15:40:16Z
dc.date.available2024-02-16T15:40:16Z
dc.date.issued2015-05-28
dc.description.abstractPure and doped Zn1-xMgxO films were deposited onto glass substrate by ultrasonic spray pyrolysis technique. The variation of lattice constant and the blue shift of near-band-edge emission indicate that Zn2? ions are successfully substituted by Mg2? ions within ZnO lattice. At higher Mg content (x C 0.21), a drastic change appears in the morphology, as a result of structural changes from wurtzite (ZnO) structure into a mixture of wurtzite and cubic (MgO) phases. FTIR study indicated the existence of distinct characteristic absorption peaks at *442 cm-1 for Zn–O stretching mode that shifted toward the red region with the increase in Mg content. In addition to the host phonons of ZnO, one additional band was observed around 523 cm-1, presumably attributed to the Mgrelated vibrational mode. The optical constants and thickness of thin films have been determined using experimental transmittance data. The luminescence intensity at 2.63 eV of Zn0.85Mg0.15O thin films was found to be approximately 13 times higher than that of pure ZnO film measured under the same excitation conditions
dc.identifier.urihttp://dspace.univ-khenchela.dz:4000/handle/123456789/1301
dc.language.isoen
dc.titleStructural, microstructural, and optical properties of Zn12xMgxO thin films grown onto glass substrate by ultrasonic spray pyrolysis
dc.title.alternativeStructural, microstructural, and optical properties of Zn12xMgxO thin films grown onto glass substrate by ultrasonic spray pyrolysis
dc.typeArticle
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
Structural, microstructural, and optical properties of Zn12xMgxO-1.pdf
Size:
2.47 MB
Format:
Adobe Portable Document Format
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed to upon submission
Description:
Download
Collections
scientific publication