Influence of the carburization time on the structural and mechanical properties of XC20 stee

Simple item page
dc.contributor.authorSaoudi Abdenour
dc.contributor.authorAissani Linda
dc.contributor.authorChahaoui Oualid
dc.contributor.authorBestandji Ali
dc.contributor.authorLouafi Med Salah
dc.contributor.authorDjebaili Hamid
dc.date.accessioned2024-02-13T02:32:59Z
dc.date.available2024-02-13T02:32:59Z
dc.date.issued2021-08-21
dc.descriptionThis study focuses on the effect of carburization time on the structural and mechanical properties of low carbon XC20 mild steel(C. Wt.% <0.25). The XC20 steel was carburized with activated carbon with a carbon potential Cp1 = 1.1%, at 910 °C at different carburization times of 2, 4 and 6 h. The results obtained show that XC20 steel(non-carburized) has a ferrite-pearlitic structure with a hardness and a Young’s modulus of the order of (150 HV, 26 KN/mm2 ). After carburization, the structure of the carburized layer is transformed in martensite (Fe γ)in which cementite (Fe3C)is imbricated. The depth of the carburized layer and the amount of carbon on the surface gradually increase with increasing carburization time. In addition, the carburized XC20 steel becomes hard and brittle where the hardness and Young’s modulus have been increased for a high holding time until reaching maximum values(845 HV, 48 KN mm−2 ) after 6 h of carburization . However, the toughness of XC20 steel has been reduced from 163 to 40 J cm−2 .
dc.description.abstractThis study focuses on the effect of carburization time on the structural and mechanical properties of low carbon XC20 mild steel(C. Wt.% <0.25). The XC20 steel was carburized with activated carbon with a carbon potential Cp1 = 1.1%, at 910 °C at different carburization times of 2, 4 and 6 h. The results obtained show that XC20 steel(non-carburized) has a ferrite-pearlitic structure with a hardness and a Young’s modulus of the order of (150 HV, 26 KN/mm2 ). After carburization, the structure of the carburized layer is transformed in martensite (Fe γ)in which cementite (Fe3C)is imbricated. The depth of the carburized layer and the amount of carbon on the surface gradually increase with increasing carburization time. In addition, the carburized XC20 steel becomes hard and brittle where the hardness and Young’s modulus have been increased for a high holding time until reaching maximum values(845 HV, 48 KN mm−2 ) after 6 h of carburization . However, the toughness of XC20 steel has been reduced from 163 to 40 J cm−2 .
dc.identifier.issnhttps://www.researchgate.net/publication/353992063_Influence_of_the_carburization_time_on_the_structural_and_mechanical_properties_of_XC20_steel
dc.identifier.urihttp://dspace.univ-khenchela.dz:4000/handle/123456789/575
dc.language.isoen
dc.publisherMater. Res. Express
dc.relation.ispartofseriesVol.8(8) 2021
dc.titleInfluence of the carburization time on the structural and mechanical properties of XC20 stee
dc.typeArticle
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
Influence of the carburization time on the structural and mechanical properties of XC20 steel (H.Djebaili 2021).pdf
Size:
198.32 KB
Format:
Adobe Portable Document Format
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed to upon submission
Description:
Download
Collections
scientific publication