Deposition Rate and Electrochemical Corrosion Behavior of Nickel-Based Composite Coatings
No Thumbnail Available
Date
2022-12-27
Authors
Journal Title
Journal ISSN
Volume Title
Publisher
JOURNAL OF NANO- AND ELECTRONIC PHYSICS
Abstract
Metal corrosion control is technically, economically, environmentally and aesthetically important. The
best option is to use coatings to protect metals and alloys from corrosion. Nickel plating is one of the most
widely used methods for protecting less noble metal surfaces since the turn of the century. The need for
improved coatings with better wear and corrosion resistance has led to the development and use of composite
electrostatic deposits. In this paper, Ni-P-TiO2 composite coatings were fabricated by direct current
electrodeposition on copper substrates. X-ray diffraction (XRD) analysis and energy dispersive spectroscopy
(EDS) were employed to determine the average particle size of coatings elemental chemical composition.
The electrochemical corrosion behavior of Ni-P-TiO2 composite coatings in 3.5 wt. % NaCl was characterized
using a potentiodynamic polarization test and electrochemical impedance spectroscopy (EIS). The results
indicate that TiO2 nanoparticles are included in the coatings. The deposition rate increased with increasing
current density; the microhardness of the coatings noticeably increased with current density. Corrosion
tests have shown that 3 A.dm – 2 is the optimal value of the applied current density in terms of the
lowest value Ecorr – 504 mV and the best charge transfer resistance Rp 114.7 Ω.cm2.
Description
Keywords
Citation
F. LEKMINE, I. ZIDANI, A. CHALA, H. BEN TEMAM, Deposition Rate and Electrochemical Corrosion Behavior of Nickel-Based Composite Coatings,JOURNAL OF NANO- AND ELECTRONIC PHYSICS, Vol. 14 No 6, 06005(5pp) (2022)