THE INFLUENCE OF SALT BATH NITRIDING VARIABLES ON HARDNESS LAYER OF AISI 1045 STEEL

Simple item page
dc.contributor.authorGhelloudj Elhadj
dc.contributor.authorDjebaili Hamid
dc.contributor.authorHannachi Med Tahar
dc.contributor.authorSaoudi Abdenour
dc.date.accessioned2024-02-13T01:18:21Z
dc.date.available2024-02-13T01:18:21Z
dc.date.issued2016-09-27
dc.descriptionThe aim of this paper is to study and analyze the effects of a surface controlled salt bath nitriding on the microhardness of AISI 1045 steel. The nitriding process was implemented in the salt bath component at ten different times (from 1 h to 10 h) when the temperature was constant at (520ºC). The nitriding process repeated of other specimens at the same times, but the temperature was (580ºC).The microstructure of the surface layers was investigated by scanning electron microscopy (SEM) and optical microscopy. Hardness profiles were measured with lowload hardness testing to determine the growth of the case depth after nitriding. Microhardness testing was carried out on samples to investigate the hardness profile at the transition from the compound to the diffusion layer. The microhardness of the surface of the nitrided sample at 520ºC and 580ºC was observed in the range of 318–430 HV0.3 and 329–421 HV0.3, respectively. Experimental results showed that the nitrides ε-Fe2-3(N, C) and γ’-Fe4(N,C) present in the compound layer increase the microhardness , It also showed that the Increasing the salt bath nitriding parameters (treatment time and temperature) increases the surface hardness and hardness profile.
dc.description.abstractThe aim of this paper is to study and analyze the effects of a surface controlled salt bath nitriding on the microhardness of AISI 1045 steel. The nitriding process was implemented in the salt bath component at ten different times (from 1 h to 10 h) when the temperature was constant at (520ºC). The nitriding process repeated of other specimens at the same times, but the temperature was (580ºC).The microstructure of the surface layers was investigated by scanning electron microscopy (SEM) and optical microscopy. Hardness profiles were measured with lowload hardness testing to determine the growth of the case depth after nitriding. Microhardness testing was carried out on samples to investigate the hardness profile at the transition from the compound to the diffusion layer. The microhardness of the surface of the nitrided sample at 520ºC and 580ºC was observed in the range of 318–430 HV0.3 and 329–421 HV0.3, respectively. Experimental results showed that the nitrides ε-Fe2-3(N, C) and γ’-Fe4(N,C) present in the compound layer increase the microhardness , It also showed that the Increasing the salt bath nitriding parameters (treatment time and temperature) increases the surface hardness and hardness profile.
dc.identifier.issnhttps://www.researchgate.net/publication/309104365_The_influence_of_salt_bath_nitriding_variables_on_hardness_layer_of_AISI_1045_steel
dc.identifier.urihttp://dspace.univ-khenchela.dz:4000/handle/123456789/570
dc.language.isoen
dc.publisherActa Metallurgica Slovaca,
dc.relation.ispartofseriesVol. 22, 2016, No.3, p. 188-194
dc.titleTHE INFLUENCE OF SALT BATH NITRIDING VARIABLES ON HARDNESS LAYER OF AISI 1045 STEEL
dc.typeArticle
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
THE INFLUENCE OF SALT BATH NITRIDING VARIABLES ON HARDNESS LAYER OF AISI 1045 STEEL (H.Djebaili 2016).pdf
Size:
175.4 KB
Format:
Adobe Portable Document Format
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed to upon submission
Description:
Download
Collections
scientific publication