    Calcination products of gibbsite studied by X-ray diffraction, XPS and solid-state NMR
    (2014-03-20) A. Malki
    The changes caused by heat treatment of gibbsite powder at 300–1473 K were studied using the X-ray diffraction (XRD), X-ray photoemission (XPS) spectra and 27Al magic angle spinning nuclear magnetic resonance spectroscopy (27Al MAS NMR). XRD analysis indicates that the transformation sequence involves the formation of κ-Al2O3 as an intermediate phase between χ- and α-Al2O3. The crystallite size of χ-Al2O3 is as small as 10 nm. XPS analysis indicates that the ratio of aluminium atoms to oxygen atoms in χ-Al2O3 and κ-Al2O3 increases, whereas the expected ratio is observed in α-Al2O3. The percentage of AlO4 units in the transition aluminas follows the same behaviour as the ratio of Al/O.
  • No Thumbnail Available
    Item
    Calcination products of gibbsite studied by X-ray diffraction, XPS and solid-state NMR
    (2014-03-20) A. Malki
    The changes caused by heat treatment of gibbsite powder at 300–1473 K were studied using the X-ray diffraction (XRD), X-ray photoemission (XPS) spectra and 27Al magic angle spinning nuclear magnetic resonance spectroscopy (27Al MAS NMR). XRD analysis indicates that the transformation sequence involves the formation of κ-Al2O3 as an intermediate phase between χ- and α-Al2O3. The crystallite size of χ-Al2O3 is as small as 10 nm. XPS analysis indicates that the ratio of aluminium atoms to oxygen atoms in χ-Al2O3 and κ-Al2O3 increases, whereas the expected ratio is observed in α-Al2O3. The percentage of AlO4 units in the transition aluminas follows the same behaviour as the ratio of Al/O.
  • No Thumbnail Available
    Item
    Calcination products of gibbsite studied by X-ray diffraction, XPS and solid-state NMR
    (2014-03-20) A. Malki
    The changes caused by heat treatment of gibbsite powder at 300–1473 K were studied using the X-ray diffraction (XRD), X-ray photoemission (XPS) spectra and 27Al magic angle spinning nuclear magnetic resonance spectroscopy (27Al MAS NMR). XRD analysis indicates that the transformation sequence involves the formation of κ-Al2O3 as an intermediate phase between χ- and α-Al2O3. The crystallite size of χ-Al2O3 is as small as 10 nm. XPS analysis indicates that the ratio of aluminium atoms to oxygen atoms in χ-Al2O3 and κ-Al2O3 increases, whereas the expected ratio is observed in α-Al2O3. The percentage of AlO4 units in the transition aluminas follows the same behaviour as the ratio of Al/O